dc.description.abstractEl presente trabajo de investigación consiste en la evaluación de las variables y parámetros de soldadura para mejorar la calidad de las uniones soldadas, usando los códigos de fabricación ASME y complementando con prácticas recomendadas de entidades como API y NACE para elevar el grado de calidad y asegurar la integridad en funcionamiento de la unión soldada. Para este trabajo de investigación se utilizó como materiales base a unir un acero de baja aleación A335 Gr. P22 y un acero inoxidable A312-TP321, los datos recolectados se obtuvieron en la calificación de un procedimiento de soldadura para el proyecto de construcción de una refinería de petróleo, se plantearon ensayos destructivos y no destructivos para evaluar la calidad de la unión soldada. Para la calificación del procedimiento se utilizaron los parámetros de soldadura establecidos en el trabajo de investigación, se inició la soldadura manteniendo una temperatura de precalentamiento hasta el final, posterior a la soldadura se realizó el tratamiento de deshidrogenado para seguir con el tratamiento térmico de alivio de tensiones. Se realizó los ensayos de tintes penetrantes e inspección radiográfica para asegurar que el cupón de prueba esté libre de discontinuidades antes de ser enviado al laboratorio para la realización de los ensayos mecánicos. Con los resultados emitidos por el laboratorio se concluyó que la correcta evaluación de las variables y parámetros de soldadura aseguraron la calidad de la unión soldada.es
dc.description.abstractThe present research consists of the evaluation of welding variables and parameters to improve the quality of welded joints, using ASME manufacturing codes and complementing with recommended practices from entities such as API and NACE to raise the degree of quality and ensure the integrity in operation of the welded joint. For this research, a low alloy steel A335 Gr. P22 and a stainless steel A312- TP321 were used as base materials to join, the data collected was obtained in the qualification of a welding procedure for the construction project of an oil refinery, destructive and non-destructive tests were proposed to evaluate the quality of the welded joint. For the qualification of the procedure, the welding parameters established in the research work were used, the welding was started maintaining a preheating temperature until the end, after the welding, the dehydrogenation treatment was carried out to continue with the thermal treatment of stress relief. Penetrating dye tests and radiographic inspection were performed to ensure that the test coupon was free of discontinuities before being sent to the laboratory for mechanical tests. With the results issued by the laboratory, it was concluded that the correct evaluation of the variables and parameters of welding ensured the quality of the welded joint.en
dc.description.uriTrabajo de suficiencia profesionales
dc.formatapplication/pdfes
dc.language.isospaes
dc.publisherUniversidad Nacional de Ingenieríaes
dc.rightsinfo:eu-repo/semantics/restrictedAccesses
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/4.0/es
dc.sourceUniversidad Nacional de Ingenieríaes
dc.sourceRepositorio Institucional - UNIes
dc.subjectTecnología mecánicaes
dc.subjectSoldaduraes
dc.subjectProceso de soldadura GTAWes
dc.subjectTratamiento térmicoes
dc.titleEvaluación de las variables críticas y parámetros de soldadura para mejorar la calidad de las uniones soldadas en una refinería de petróleoes
dc.typeinfo:eu-repo/semantics/bachelorThesises
thesis.degree.nameIngeniero Mecánicoes
thesis.degree.grantorUniversidad Nacional de Ingeniería. Facultad de Ingeniería Mecánicaes
thesis.degree.levelTítulo Profesionales
thesis.degree.disciplineIngeniería Mecánicaes
thesis.degree.programIngenieríaes
renati.author.dni47525225-
renati.advisor.dni07188676-
renati.typehttp://purl.org/pe-repo/renati/type#trabajoDeSuficienciaProfesionales
renati.levelhttp://purl.org/pe-repo/renati/nivel#tituloProfesionales
renati.discipline713046-
renati.jurorGamarra Chinchay, Hugo Eliseo-
renati.jurorSarmiento Sarmiento, Enrique-
dc.publisher.countryPEes
dc.subject.ocdehttp://purl.org/pe-repo/ocde/ford#2.03.01es
Aparece en las colecciones: Ingeniería Mecánica

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
quispe_ql.pdf9,47 MBAdobe PDFVisualizar/Abrir
quispe_ql(acta).pdf83,61 kBAdobe PDFVisualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons

Indexado por:
Indexado por Scholar Google LaReferencia Concytec BASE renati ROAR ALICIA RepoLatin UNI